CHARACTERISTIC |
UNIT |
|
|
|
|
|
|
Specific gravity
ASTM D 792 |
gr/cm^3 |
1.21 |
1.22 |
1.23 |
1.23 |
1.24 |
1.25 |
Shore Hardness
ASTM D 2240 |
A
D |
82
|
86
|
91
|
50 |
57 |
65 |
Abrasion loss
DIN 53516 |
mm^3 |
30 |
35 |
35 |
35 |
40 |
40 |
Tensile Modulus
ASTM D 412 |
50% MPa
psi
100% Mpa
psi
300% MPa
psi |
3.8
540
5.3
760
10.2
1500
|
4.9
700
6.8
970
14.9
2100
|
7.0
1000
8.8
1300
20.5
2900
|
8.2
1200
10.6
1500
26.8
3800
|
15.2
2200
17.5
2500
38.0
5400
|
19.5
2800
22.5
3200
44.0
6300 |
Tensile Strength
ASTM D 412 |
MPa
psi |
48.2
6900
|
51.6
7400
|
54.8
7800
|
58.1
8300
|
63.2
9000
|
64.7
9200 |
Elongation at break
ASTM D 412 |
% |
590 |
550 |
500 |
470 |
450 |
420 |
Tear Strength
ASTM D 624 |
N/mm |
78 |
95 |
108 |
132 |
160 |
190 |
Flexural Modulus
ASTM D 790 |
MPa
psi |
|
|
|
75
11000
|
180
26000
|
360
52000 |
Torsion Test
ASTM D 1043 |
+20°C MPa
psi
-20°C MPa
psi |
|
|
|
20
2900
190
27000 |
46
6600
354
51000
|
77
11000
455
65000 |
Vicat Soft. point
ASTM D 1525 |
°C
°F |
84
183 |
86
187
|
100
210
|
105
221
|
126
259
|
150
302 |
Comp. Set
ASTM D 395 |
70h/23°C %
22h/70°C %
70h/100°C % |
18
41
|
21
43
|
22
45
|
24
50
|
|
|
Impact Test
ASTM D 256 -20°C |
KJ/m^2 |
|
|
|
|
|
|
Flammability Test UL 94
(vertical burning) |
|
|
|
|
|
|
|
| Processing |
injection
extrusion |
0
|
0
|
0
|
0
|
0
|
0
|
| Features |
|
|
|
|
|
|
|